0.1mm Thickness White Hot Melt Adhesive For Battery Tab

Model

TOB-W-TTP

Color

Milk-White

Thickness

100 um

Width

4mm, 5mm, 6mm, 7mm, 8mm,10mm, Customized width

Length

500m for 1 roll

Material

Enhanced Sulfurized Polymer Resin Material (3 Layers Lamination)

Outside Layers (Both Sides) 

Thermal Softening Index

116ºC/ 3 Seconds/ 0.3Mpa/ 180ºC (Reference only)

Outside Layers

 (Both Sides) Thermal Melting Index

135ºC/ 3 Seconds/ 0.3Mpa/ 180ºC (Reference only)

Middle Layers (Both Sides) 

Thermal Softening Index

145ºC/ 3 Seconds/ 0.3Mpa/ 180ºC (Reference only)

Middle Layers (Both Sides) 

Thermal Melting Index

175ºC/ 3 Seconds/ 0.3Mpa/ 180ºC (Reference only)

Removal Strength from Tab

> 15N/15mm

Removal Strength from 

Al Lamination Film (Cell Case)

> 35N/15mm

Resistance to LiPF6 Solution (1:1:1)

No Change in the Solution @ 85ºC*24 Hours